今天就让小编为大家详细的介绍环氧地坪漆起皮的相关知识，如环氧地坪漆起皮产生的原因、施工人员的过错或者是施工人员的经验缺乏、产质量量要素、底漆挑选不妥、环氧地坪施工失利导致很快起皮最可能的原因是什么？希望对你们有所帮助。环氧地坪漆起皮产生的原因

Today let Xiaobian introduce in detail the relevant knowledge of epoxy floor paint peeling, such as the cause of epoxy floor paint peeling, the fault of builders or lack of experience of builders, factors of production and quality, inappropriate selection of primer, failure of epoxy floor construction, what is the most likely cause of rapid peeling? I hope it will help you. Reasons for Skinning of Epoxy Floor Paint １.环氧地坪漆涂装前处理欠安，被涂物外表上有油污、蜡、水汽、尘埃和化学药品等。或外表预处理后至涂漆旅工的间隔时刻过长涂装前被涂物外表应处理清洁，并应立即涂装施工。

1. The pretreatment of epoxy floor paint is unsafe. There are oil, wax, vapor, dust and chemicals on the surface of the paint. or the time interval between pretreatment and painting travelers is too long. Before painting, the appearance of the coated objects should be cleaned and immediately painted.

２.底漆挑选不妥，建材底漆分为高浸透底漆和密封型底漆两种，如底漆挑选不妥也会形成环氧地坪起皮。底漆的硬度过大涂膜外表太滑润。都会使面漆和底漆间失掉应有的黏附力应选用附着力和湿润性好的底漆。

2. Inappropriate selection of primers, building materials primers are divided into high-permeability primers and sealed primers, such as improper selection of primers will form floor peeling. The hardness of the primer is too high and the surface of the coating is too smooth. The primer with good adhesion and wettability should be chosen when the adhesion between the top coat and the primer is lost.

３.被涂物外表太润滑，被涂物外表应打磨或经化学处理。旧漆面应从头打磨处理。

3. The surface of the coated material is too lubricated. The surface of the coated material should be polished or chemically treated. Old paint should be ground from scratch.

４.环氧地坪漆配套不恰当，经过实验挑选配套性杰出的涂料种类及改用“湿碰湿”工艺。或添加中心涂层。

4. The matching of epoxy floor paint is inappropriate. The excellent matching coatings are selected through experiments and the "wet touch" process is modified. or add a central coating.

５.在底漆未干透之前就涂刮腻子或涂涂刷面漆或清漆。漆膜易发作开裂或掉落，一般应在底漆彻底干透后再进行下一道工序。在湿润或霉染的物面上涂装。使漆与底材附着不良砖石、水泥等物面应充沛枯燥和除掉霉染物后再涂装施工。涂膜太厚，由于表层已干透。而底层干得慢或未干透。在枯燥过程中由于面漆缩短过甚而引起开裂掉落施工中应留意每道漆的漆膜不宜太厚。

5. Scrape putty or paint or varnish before the primer is dry. The film is liable to crack or fall off. Usually, the next process should be carried out after the primer is thoroughly dried out. Paint on wet or mouldy surfaces. The surface of masonry, cement and other materials with poor adhesion between paint and substrates should be plentifully dry and be painted after removing mildew and dyes. The film is too thick because the surface is dry. The bottom is slow or not dry. In the process of drying, cracks and drops caused by over-shortening of topcoat should be noticed that the film of each paint should not be too thick.